Method for producing silicone elastomer molds

ABSTRACT

Silicone compositions are described for the production of negative molds that include a silicone elastomer. The molds can be used in the production of molded articles.

The field of the invention relates to the use of silicone compounds forthe manufacture of negative molds formed from silicone elastomer for usein the manufacture of molded articles.

Bicomponent organopolysiloxane compositions that can be used for thepreparation of molds produced from silicone elastomer have already beenproposed on the industrial market and in the chemical literature (FR 1418 114 and JP 50066553). These compositions may include a variety ofadditives (which facilitate processing them or transforming them intoelastomers), such as low viscosity dihydroxydiorganopolysiloxane oils(FR 2 272 145 and FR 2 300 114).

Patent application EP 586 153 describes a curable silicone compositioncomprising, in addition to the constituents which are routinely used insuch a composition, reinforcing co-fillers such as acicular fillersbased on CaO and SiO₂, or in fact on CaSiO₃; and ceramic-based sphericalfillers, and in particular on silica-alumina ceramics.

Another approach is described in the document EP 787 766. That documentdescribes silicone compositions which can be cured at ambienttemperature by condensation in order to produce molds, furthercomprising the constituents which are conventionally used in this typeof composition, additives selected from the group constituted bysterically hindered phenols, sterically hindered thio bisphenols, zincdialkyl dithiophosphates, zinc diaryl dithiophosphates, aromatic amines,sterically hindered amines, or in fact preparations based on thosecompounds.

Patent application WO 03/074602 describes the use of silica pre-treatedin a silicone composition which can be cured by polycondensation, as astabilization agent for molds obtained from that composition.

Patent application WO 06/106238 teaches a method for stabilizing moldscomposed of a silicone elastomer.

Among the silicone compositions that can be cured to produce anelastomer which are known for this type of application, those which curefrom ambient temperature form a category which catches the attention,because they do not have to be placed in an energy-consuming oven.

These silicone compositions are classified into 2 distinct groups:monocomponent compositions (RTV-1) and bicomponent compositions (RTV-2).The term “RTV” is the acronym for “Room Temperature Vulcanizing”.

During curing, water (either supplied via moisture from the atmospherein the case of RTV-1, or introduced into a part of the composition inthe case of RTV-2) allows the polycondensation reaction to take place,which leads to the formation of the elastomeric network.

In general, monocomponent compositions (RTV-1) cure when they areexposed to the moisture of the air. Usually, the polycondensationreaction kinetics are extremely slow: these reactions are thereforecatalyzed by an appropriate catalyst.

Regarding bicomponent compositions (RTV-2), these are sold and stored inthe form of two components, a first component containing the basicpolymer materials and the second component containing the catalyst. Thetwo components are mixed for use and the mixture cures into the form ofa relatively hard elastomer. These bicomponent compositions are wellknown and have in particular been described in the work by Walter Noll,“Chemistry and Technology of Silicones” 1968, 2^(nd) edition, pages 395to 398.

These compositions essentially comprise 4 different ingredients:

-   a reactive α,ω -dihydroxydiorganopolysiloxane polymer,-   a curing agent, generally a silicate or a polysilicate,-   a catalyst, and-   water.

The mechanical properties of these compositions are then adjusted byadding fillers.

Usually, the condensation catalyst is based on an organic tin compound.In fact, many tin-based catalysts have already been proposed as acatalyst for curing these RTV-1s or RTV-2s. Conventionalpolycondensation catalysts comprise dialkyltin compounds, in particulardialkyltin dicarboxylates such as dibutyltin dilaurate and diacetate,alkyl titanate compounds such as tetrabutyl or tetraisopropyl titanate,and titanium chelates (EP-A-0 885 933, US-5 519 104, US-A-4 515 932,US-A-4 563 498, US-A-4 528 353).

However, alkyltin-based catalysts, while being highly efficient, andusually colorless, liquid and soluble in silicone oils, suffer from thedisadvantage of being toxic (CMR2 toxic for reproduction).

In addition, in the face of a molding industry which is evolving rapidlywith the development of 3D printing, fresh constraints are appearingwhich are linked to the increase in successive molding/demolding cycles.

For sustainable development, there is an ongoing need for improvementsto methods for the preparation of negative molds produced from siliconeelastomer starting from silicone compositions that cure bypolycondensation in the absence of tin, while improving the resistanceto successive molding/demolding cycles carried out on said moldsobtained. The silicone compositions must also have suitable curingkinetics and good stability on storage. Preferably, in the absence of arelease agent applied to the master to be reproduced, the negative moldsproduced from silicone must not adhere to said master.

Thus, one of the essential aims of the present invention is to propose anovel method for the preparation of negative molds produced fromsilicone elastomer that can be used for the manufacture of moldedarticles in which the silicone elastomer is prepared from a siliconecomposition that does not contain a metallic catalyst such as tin, forexample, and which cures by polycondensation reactions in the presenceof water (for example ambient moisture) with a curing rate that issufficient to ensure industrial rates of production.

A further aim is to propose a novel method for forming molded articlesstarting from a negative mold produced from silicone elastomer having agood resistance to successive molding/demolding cycles and prepared fromsilicone compositions containing no tin.

A further aim is to propose a silicone composition containing no tin andhardening to form a silicone elastomer in the presence of moisture withrapid surface solidification kinetics, followed by a complete coresolidification, i.e. homogeneous solidification, in a manner such as toprepare negative molds produced from silicone elastomers which do notadhere on the one hand to the master to be reproduced and on the otherhand to the molded articles, and thus have a good resistance tosuccessive molding/demolding cycles and which can be used for thepreparation of molded articles produced from different materials.

The invention also concerns negative molds produced from siliconeelastomer for use in the manufacture of molded articles produced fromdifferent reproduction materials such as from polyester, polystyrene,polyethylene, polyvinyl chloride, polyurethane, polyurethane foam,plaster, concrete, wax and soap. This list is not limiting.

The parts molded from different reproduction materials that are obtainedrepresent a wide variety of articles, with a utilitarian or decorativepurpose, such as dashboards, armrests, furniture, or works of art.

These aims, inter alia, are achieved by means of the present invention,which concerns a method for preparing a negative mold MN produced fromsilicone elastomer for use in the manufacture of molded articlesproduced from different reproduction materials, characterized in that itcomprises the following steps a) to d) :

-   a) preparing a polyorganosiloxane composition X that can be cured to    produce an elastomer by polycondensation reactions, which does not    contain a metallic catalyst, and comprising:    -   -- a silicone base B comprising at least one polyorganosiloxane        oil A that can be cured by a polycondensation reaction, and    -   a catalytically effective quantity of at least one        polycondensation catalyst C, which is an organic compound having        the general formula (I): (R″)₂NH

    in which the symbols R″, which may be identical or different,    represent aliphatic hydrocarbon radicals containing 1 to 30 carbon    atoms,-   b) applying said polyorganosiloxane X to a master to be duplicated,    optionally already covered with a release agent,-   c) allowing said polyorganosiloxane composition X to cure in the    presence of moisture supplied by the ambient air or by the prior    addition of water, in order to form a negative mold MN produced from    silicone elastomer, which is an impression corresponding to the    exterior contour of the master to be duplicated, and-   d) separating the negative mold MN produced from silicone elastomer    from the master to be duplicated.

One advantage linked to the method in accordance with the invention isthat the number of cycles for molding/demolding articles molded in thisnegative mold MN is preferably more than 37, for example when demoldingpolyurethane replicas.

The technique for molding in silicone elastomer consists of producing a“negative” mold, i.e. an impression, from a “positive” model termed the“master”. The silicone elastomer mold that is generated thereby can beused to produce many “copies” or “prints” or “replicas” from the master,with no limits as to size or undercuts.

A variety of molding techniques are known to the person skilled in theart. Examples of molding techniques that may be cited are:

-   “block molding”, which is intended for the manufacture of    self-supporting molds, produced from one or more parts, by simple    casting of the composition over the initial master inside a sealed    counter-mold after mixing the two parts of the RTV-2 in the liquid    state. This method is preferred for relatively simple shapes without    major undercuts;-   “one or two-part shell molding”, and-   “stamping molding”, which is preferred for taking an impression of    inclined, vertical or overhanging masters, in general with large    dimensions, or when it is impossible to move the master.

When using the compositions in accordance with the invention in thisapplication, casting techniques or techniques for application by meansof a spatula, brush or by spraying are useful.

The manufactured molds have the particular feature of reproducing thedetails of the masters accurately and in fine detail; furthermore,because of the non-stick nature of silicone rubber, they can improvedemolding rates.

A release agent may, however, be applied to the item to be reproducedprior to molding it. These release agents are well known to the personskilled in the art. By way of non-limiting example, it is possible touse an aqueous solution of soap or a suspension of wax.

In a further aspect, the present invention concerns a method for moldingreplicas R, characterized in that it comprises steps a) to d) inaccordance with the invention, followed by the following steps e) to h):

-   e) filling this negative mold MN produced from silicone elastomer    with a reproduction material,-   f) allowing the reproduction material to harden inside the negative    mold MN produced from silicone elastomer, in order to produce a    replica R of the master to be duplicated,-   g) separating the replica R from the negative mold MN produced from    silicone elastomer, and-   h) optionally, submitting the negative mold MN produced from    silicone elastomer to steps e) to g) again, in order to form a new    replica R.

An advantage linked to the method in accordance with the invention isthat the number of cycles e) to g) that can be carried out with thenegative mold MN produced from silicone elastomer is more than 37, forexample when demolding polyurethane replicas.

Various reproduction materials are known to the person skilled in theart, such as polyester, polystyrene, polyethylene, polyvinyl chloride,polyurethane, polyurethane foam, plaster, concrete, wax and soap. Thislist is not limiting. Before molding, these reproduction materials arein different forms, namely liquid which is viscous to a greater orlesser extent, a dispersion, suspension, with a single or with multiplecomponents.

More precisely, the present invention concerns an organopolysiloxanecomposition that can be vulcanized to form a silicone elastomer fromambient temperature by polycondensation reactions comprising:

-   (a) a silicone base that is capable of hardening into a silicone    elastomer in the presence of a catalyst by polycondensation    reactions, comprising:    -   for 100 parts by weight of at least one        α,ω-dihydroxydiorganopolysiloxane A,    -   0.1 to 60 parts by weight of at least one curing agent AR, and    -   0.001 to 10 parts by weight of water, and-   (b) a catalytically effective quantity of a polycondensation    catalyst C.

The reactive α,ω-dihydroxydiorganopolysiloxane polymers A that may beused in the silicone bases in accordance with the invention are moreparticularly those having the following formula (1):

in which formula:

-   the substituents R¹, which may be identical or different, each    represent a monovalent C₁ to C₁₃ hydrocarbon, which may or may not    be saturated, which may or may not be substituted, aliphatic, cyclic    or aromatic, and preferably R¹ is methyl; and-   n has a sufficient value to provide the polyorganosiloxane with    formula (1) with a dynamic viscosity at 25° C. of 10 to 1000000    mPa.s.

It should be understood that, in the context of the present invention, amixture constituted by a plurality of hydroxylated polyorganosiloxaneswhich differ among themselves by the value of the viscosity and/or thenature of the substituents bonded to the silicon atoms may be used asthe reactive polyorganosiloxane A. It should also be pointed out thatthe hydroxylated polyorganosiloxanes with formula (1) may optionallycomprise motifs T with formula R¹SiO_(3/2) and/or motifs Q with formulaSiO_(4/2) in a proportion of at most 1% (these % expressing the numberof T and/or Q motifs per 100 silicon atoms).

Reactive linear hydroxylated diorganopolysiloxane polymers A with adynamic viscosity at 25° C. of 10 to 1000000 mPa.s and preferably from50 to 200000 mPa.s are employed.

These basic polyorganosiloxanes are for the most part marketed bysilicone manufacturers. In addition, their manufacturing techniques arewell known: they are described, for example, in French patents FR-A-1134 005, FR-A-1 198 749, and FR-A-1 226 745.

All of the viscosities in question in the present description correspondto a dynamic viscosity parameter at 25° C. known as “Newtonian”, i.e.the dynamic viscosity, which is measured, in a manner which is known perse, using a Brookfield viscosimeter at a shear rate gradient which issufficiently low for the measured viscosity to be independent of thespeed gradient.

The substituent R¹ mentioned above for the reactive polyorganosiloxanes(A) may be selected from the following radicals:

-   alkyl and haloalkyl radicals containing 1 to 13 carbon atoms, such    as methyl, ethyl, propyl, isopropyl, butyl, pentyl, hexyl,    2-ethylhexyl, octyl, decyl, 3,3,3-trifluoropropyl,    4,4,4-trifluorobutyl, 4, 4, 4, 3, 3-pentafluorobutyl radicals,-   cycloalkyl and halocycloalkyl radicals containing 5 to 13 carbon    atoms, such as cyclopentyl, cyclohexyl, methylcyclohexyl,    propylcyclohexyl radicals, 2,3-difluorocyclobutyl, 3,    4-difluoro--5--methylcycloheptyl,-   alkenyl radicals containing 2 to 8 carbon atoms, such as vinyl,    allyl, buten-2-yl radicals,-   mononuclear aryl and haloaryl radicals containing 6 to 13 carbon    atoms, such as phenyl, tolyl, xylyl, chlorophenyl, dichlorophenyl,    trichlorophenyl radicals, and-   cyanoalkyl radicals the alkyl links of which contain 2 to 3 carbon    atoms, such as β-cyanoethyl and γ-cyanopropyl radicals.

Examples of radicals R¹ that may be cited are alkyl radicals containing1 to 8 carbon atoms, such as methyl, ethyl, propyl, butyl, hexyl andoctyl, vinyl radicals, and phenyl radicals.

Examples of substituted radicals R¹ that may be cited are 3, 3,3-trifluoropropyl, chlorophenyl and betacyanoethyl radicals.

In the products with formula (1) in general industrial use, at least 60%by number of the radicals R¹ are methyl radicals, the other radicalsgenerally being phenyl and/or vinyl radicals.

The following curing agents AR may be cited:

-   silanes with the following general formula (2):

-   

-   in which the symbols R³, which may be identical or different,    represent alkyl radicals containing 1 to 8 carbon atoms such as    methyl, ethyl, propyl, butyl, pentyl, 2-ethylhexyl radicals, C₃-C₆    oxyalkylene radicals, the symbol R² representing a saturated or    unsaturated, linear or branched aliphatic hydrocarbon group, a    saturated or unsaturated and/or aromatic, monocyclic or polycyclic    carbocyclic group, and k is equal to 0 or 1; and

-   partial hydrolysis and condensation products of a silane with    formula (2).

Examples of C₃-C₆ oxyalkylene radicals that may be cited are thefollowing radicals:

Advantageously, the symbol R² represents a C₁-C₁₀ hydrocarbon radicalencompassing:

-   C₁-C₁₀ alkyl radicals such as methyl, ethyl, propyl, butyl, pentyl,    2-ethylhexyl, octyl, decyl radicals,-   vinyl, allyl radicals, and-   C₅-C₈ cycloalkyl radicals such as phenyl, tolyl and xylyl radicals.

The curing agents AR with formula (2) are products that are available onthe silicones market; in addition, their use in ambienttemperature-curing compositions is known; they are mentioned inparticular in the French patents FR-A-1 126 411, FR-A-1 179 969, FR-A-1189 216, FR-A-1 198 749, FR-A-1 248 826, FR-A-1 314 649, FR-A-1 423 477,FR-A-1 432 799 and FR-A-2 067 636.

More particularly preferred of the curing agents AR arealkyltrialkoxysilanes, alkyl silicates and alkyl polysilicates, in whichthe organic radicals are alkyl radicals containing 1 to 4 carbon atoms.

The alkyl silicates may be selected from methyl silicate, ethylsilicate, isopropyl silicate, n-propyl silicate and polysilicatesselected from the products of partial hydrolysis and condensation ofthese silicates; these are polymers constituted by a large proportion ofmotifs with formula: (R⁴O)₃SiO_(½), R⁴OSiO_(3/2), (R⁴O)₂SiO_(2/2) andSiO_(4/2); the symbol R⁴ representing methyl, ethyl, isopropyl and/orn-propyl radicals. They are usually characterized on the basis of theirsilicon content, which is established by assaying the hydrolysis productof a sample.

Other examples of curing agents AR that may be used and that may inparticular be cited are the following silanes:

-   CH₃Si (OCH₃)₃; C₂H₅Si (OC₂H₅)₃; C₂H₅Si (OCH₃)₃-   CH₂=CHSi (OCH₃)₃; CH₂=CHSi (OCH₂CH₂OCH₃)₃-   C₆H₅Si (OCH₃)₃; [CH₃] [OCH (CH₃) CH₂OCH₃] Si [OCH₃] ₂-   Si (OCH₃) ₄; Si (OC₂H₅) ₄; Si (OCH₂CH₂CH₃)₄; Si (OCH₂CH₂CH₂CH₃) ₄ Si    (OC₂H₄OCH₃)₄; CH₃Si (OC₂H₄OCH₃)₃; ClCH₂Si (OC₂H₅)₃.

Other examples of the curing agent AR that may be cited are ethylpolysilicate or n-propyl polysilicate.

In general, 0.1 to 6 parts by weight of curing agent with formula (2)are used per 100 parts by weight of reactive polymer with formula (1).

Organic compounds from the secondary amine family with the followinggeneral formula (I) may be cited as the catalyst C:

in which the symbols R″, which may be identical or different, representaliphatic hydrocarbon radicals containing 1 to 30 carbon atoms,preferably 4 to 12 carbon atoms and more preferably those containing 6to 10 carbon atoms.

Preferably, during step a) of the methods in accordance with theinvention, the polycondensation C has the general formula (I):

in which the symbols R″, which may be identical or different, representaliphatic hydrocarbon radicals containing 6 to 10 carbon atoms,preferably 8 to 10 carbon atoms.

The catalyst C which has just been described is used to enable orfacilitate hardening into silicone elastomers, from ambient temperature,of polyorganosiloxane bases that can be cured by polycondensationreactions in the form of a bicomponent compound, the catalytic systembeing incorporated into one of the fractions with a curing agent AR,while the other fraction contains a reactive polyorganosiloxane A andwater.

In the present invention, the term “ambient temperature” means atemperature in the range 10° C. to 40° C.

In accordance with another aspect, the invention concerns apolyorganosiloxane composition X that can be cured to produce anelastomer by polycondensation reactions, which does not contain ametallic catalyst, and which comprises:

-   a silicone base B comprising at least one polyorganosiloxane oil A    that can be cured by a polycondensation reaction in a manner such as    to form a silicone elastomer, and

-   a catalytically effective quantity of at least one polycondensation    catalyst C which is an organic compound having general formula (I):

-   

-   in which the symbols R″, which may be identical or different,    represent aliphatic hydrocarbon radicals containing 6 to 10 carbon    atoms, preferably 8 to 10 carbon atoms.

In the present invention, the term “an effective quantity of at leastone polycondensation catalyst C” means a quantity in the range 0.01 to50 parts by weight of polycondensation catalyst C.

The catalysts employed in the silicone compositions used during thepreparation of silicone elastomer molds in accordance with the inventionmean that the following can be obtained at the same time:

-   a sufficiently long pot life for using the mixture of part P1 + part    P2 (between 20 and 200 min),-   “fast” curing (post-curing a maximum of +2 and SAH 24 h x 100/SAH 14    days > 68%),-   silicone elastomer molds obtained by the method in accordance with    the invention, which means that a substantial number of parts, for    example produced from polyurethane, can be molded (number of    successive molding/demolding cycles > 37),

and all this in the absence of tin-based compounds.

In order to satisfy the supplemental conditions that the part containingthe catalyst has to be homogeneous (transparent, single phase) and thatthe silicone elastomer molds obtained by the method in accordance withthe invention do not stick to the master in the absence of a releaseagent applied to the master to be reproduced, the polycondensationcatalysts C have the general formula (I):

in which the symbols R″, which may be identical or different, representaliphatic hydrocarbon radicals containing 6 to 10 carbon atoms.

The compositions in accordance with the invention may furthermorecomprise reinforcing or semi-reinforcing fillers or packing fillers CH,which are preferably selected from siliceous fillers.

The reinforcing fillers are preferably selected from fumed silicas andprecipitated silicones. They generally have a specific surface area,measured using BET methods, of at least 50 m²/g, preferably more than 70m²/g, a mean primary particle dimension of less than 0.1 µm(micrometers) and an apparent density of less than 200 g/liter.

These silicas may be incorporated as is or after having been treatedwith organosilicon compounds that are normally employed for this use.These compounds include methylpolysiloxanes such ashexamethyldisiloxane, octamethyldisiloxane,octamethylcyclotetrasiloxane, methylpolysilazanes such ashexamethyldisilazane, hexamethylcyclotrisilazane, chlorosilanes such asdimethylchlorosilane, trimethylchlorosilane, methylvinyldichlorosilane,dimethylvinylchlorosilane, alkoxysilanes such asdimethyldimethoxysilane, dimethylvinylethoxysilane andtrimethylmethoxysilane.

During this treatment, the initial weight of the silicas can increase byup to an amount of 20%.

The semi-reinforcing fillers or packing fillers have a particle diameterof more than 0.1 µm (micrometer) and are selected from ground quartz,calcined clays and diatomaceous earth.

In addition to the principal constituents A, AR, C and CH, non-reactivelinear polyorganosiloxane polymers E may be introduced with the aim ofacting on the physical characteristics of the compositions in accordancewith the invention and/or on the mechanical properties of the elastomersobtained from hardening these compositions.

These non-reactive linear polyorganosiloxane polymers E are well known;more particularly, they comprise:α,ω-bis(triorganosiloxy)diorganopolysiloxanes with viscosities of atleast 10 mPa.s at 25° C., essentially formed by diorganosiloxy motifsand at most 1% of monoorganosiloxy and/or siloxy motifs, the organicradicals bonded to the silicon atoms being selected from methyl, vinyland phenyl radicals, at least 60% of these organic radicals being methylradicals and at most 10% being vinyl radicals. The viscosity of thesepolymers may be as high as several tens of millions of mPa.s at 25° C.;thus, they include oils with a fluid to viscous appearance, and soft tohard gums. They are prepared in accordance with the usual techniquesdescribed more precisely in the French patents FR-A-978 058, FR-A-1 025150, FR-A-1 108 764, and FR-A-1 370 884. Preferably, α,ω-bis(trimethylsiloxy) dimethylpolysiloxane oils with a viscosity of 10mPa.s to 1000 mPa.s at 25° C. are used. These polymers act asplasticizers and may be introduced in an amount of at most 70 parts,preferably 5 to 20 parts, per 100 parts of reactiveα,ω-dihydroxydiorganopolysiloxane polymer A.

The compositions in accordance with the invention may furthermoreadvantageously comprise at least one silicone resin G. These siliconeresins are branched organopolysiloxane polymers which are well known andcommercially available. Per molecule, they have at least two differentmotifs selected from those with formula R‴₃SiO_(½) (motif M),R‴₂SiO_(2/2) (motif D), R‴SiO_(3/2) (motif T) and SiO₄,₂ (motif Q). Theradicals R‴ are identical or different and are selected from linear orbranched alkyl radicals, vinyl, phenyl, 3,3,3-trifluoropropyl radicals.Preferably, the alkyl radicals contain 1 to 6 carbon atoms inclusive.More particular radicals R‴ that may be cited are methyl, ethyl,isopropyl, tertiobutyl and n-hexyl radicals. These resins are preferablyhydroxylated, and in this case have a weight content of the hydroxygroup in the range 5 to 500 meq/100 g.

Examples of resins that may be cited are MQ resins, MDQ resins, TDresins and MDT resins.

In accordance with an embodiment of the invention, thepolyorganosiloxane composition X comprises:

-   (a) the silicone base B, which is capable of hardening to form a    silicone elastomer in the presence of a catalyst by polycondensation    reactions comprising:    -   for 100 parts by weight of at least one reactive        a,ω-dihydroxydiorganopolysiloxane polymer A wherein the organic        radicals are hydrocarbon radicals preferably selected from the        group constituted by: alkyls containing 1 to 20 carbon atoms;        cycloalkyls containing 3 to 8 carbon atoms; alkenyls containing        2 to 8 carbon atoms and cycloalkenyls containing 5 to 8 carbon        atoms;    -   0.1 to 60 parts by weight of at least one curing agent AR        selected from the group constituted by: polyalkoxysilanes, the        products deriving from the partial hydrolysis of a        polyalkoxysilane and polyalkoxysiloxanes;    -   0 to 250 parts by weight, preferably 5 to 200 parts by weight,        of at least one filler CH;    -   0.001 to 10 parts by weight of water,    -   0 to 100 parts by weight of at least one linear nonreactive        polyorganosiloxane polymer E consisting of a linear homopolymer        or copolymer wherein, per molecule, the monovalent organic        substituents bonded to the silicon atoms, which may be identical        or different, are selected from alkyl, cycoalkyl, alkenyl, aryl,        alkylarylene and arylalkylene radicals,    -   0 to 20 parts by weight of a coloring base or a coloration agent        F,    -   0 to 70 parts by weight of polyorganosiloxane resins G, and    -   0 to 20 parts of auxiliary additives A known to the person        skilled in the art, such as plasticizers, curing inhibitors,        mineral oils, antimicrobial agents, heat resisting additives        such as titanium, iron or cerium oxide, and-   (b) 0.01 to 50 parts by weight of a polycondensation catalyst C.

In order to use the silicone compositions X in accordance with theinvention, each composition is produced in the form of a bicomponentsystem formed by two parts P1 and P2 intended to be brought into contactwith each other in order to produce the polycondensation-curedelastomer.

In accordance with another aspect, the present invention relates to abicomponent system that is a precursor of the polyorganosiloxanecomposition X that can be vulcanized to produce a silicone elastomerfrom ambient temperature by polycondensation reactions, characterized inthat:

-   it has two distinct parts P1 and P2 intended to be mixed in order to    form said composition, and-   one of these parts comprises the catalyst c, while the other part is    free from it and comprises:    -   per 100 parts by weight of the reactive        α,ω-dihydroxydiorganopolysiloxane polymer(s) A, and    -   0.001 to 10 part(s) by weight of water.

In accordance with a preferred embodiment, the precursor bicomponentsystem of the polyorganosiloxane composition X that can be vulcanized toform a silicone elastomer from ambient temperature by thepolycondensation reactions in accordance with the invention ischaracterized in that:

-   the part P1 comprises:    -   per 100 parts by weight of the reactive        α,ω-dihydroxydiorganopolysiloxane polymer (A) wherein the        organic radicals are hydrocarbon radicals preferably selected        from the group constituted by: alkyls containing 1 to 20 carbon        atoms; cycloalkyls containing 3 to 8 carbon atoms; alkenyls        containing 2 to 8 carbon atoms and cycloalkenyls containing 5 to        8 carbon atoms;    -   0.001 to 10 parts by weight of water,    -   0 to 200 parts by weight, preferably 5 to 150 parts, of at least        one filler (CH);    -   0 to 150 parts by weight of at least one linear non-reactive        polyorganosiloxane polymer (E) consisting of a linear        homopolymer or copolymer wherein, per molecule, the monovalent        organic substituents, which may be identical or different        between them and are bonded to silicon atoms, are selected from        alkyl, cycloalkyl, alkenyl, aryl, alkylarylene and arylalkylene        radicals,    -   0 to 70 parts by weight of polyorganosiloxane resins (G), and    -   0 to 20 parts by weight of a coloring base or a coloration agent        F; and-   the part P2 comprises:    -   0.1 to 60 parts by weight of at least one curing agent AR        selected from the group constituted by: polyalkoxysiloxanes,        products deriving from the partial hydrolysis of a        polyalkoxysiloxane and polyalkoxysiloxanes;    -   0.01 to 50 parts by weight of polycondensation catalyst c,    -   0 to 20 parts by weight of a coloring base or a coloration agent        F,    -   0 to 70 parts by weight of at least one linear non-reactive        polyorganosiloxane polymer (E) consisting of a linear        homopolymer or copolymer wherein, per molecule, the monovalent        organic substituents, which may be identical or different        between them and are bonded to silicon atoms, are selected from        alkyl, cycloalkyl, alkenyl, aryl, alkylarylene and arylalkylene        radicals, and    -   0 to 125 parts by weight, preferably 0.1 to 40 parts, of at        least one filler CH.

The invention also concerns the negative mold produced from siliconeelastomer MN obtained at the end of step d) of the methods in accordancewith the invention.

The invention also concerns the use of a negative mold produced fromsilicone elastomer MN obtained at the end of step d) of the methods inaccordance with the invention, for the manufacture of molded articles.

Other advantages and characteristics of the present invention willbecome apparent from the following examples, given purely by way ofnon-limiting illustration.

EXAMPLES 1) Starting Materials Used

-   Paste preparation: Mixture of A200 fumed silica (supplied by    Evonik - 200 m²/g) treated with trimethylsilyl groups (approximately    30%) (CH1), 47V500 silicone oil (approximately 42%) (E1) and    48V14000 silicone oil (approximately 28%) (A1).-   Sifraco® E600 (supplied by Sibelco) = quartz = silica flour,    crystalline silica, ground silica (CH2)-   Bluesil® FLD 48V14000 (α,ω-dihydroxydiorganopolysiloxane oil),    viscosity 14000 mPa.s - MW approx 48 kg/mol (A1)-   Bluesil® FLD 48V3500 (α,ω-dihydroxydiorganopolysiloxane oil),    viscosity 3500 mPa.s - MW approx 30 kg/mol (A2)-   Bluesil® FLD 48V750 (α,ω-dihydroxydiorganopolysiloxane oil),    viscosity 750 mPa.s - MW approx 15 kg/mol (A3)-   Bluesil® RP 120PA (α,ω-dihydroxydiorganopolysiloxane oil), viscosity    45 mPa.s - MW approx 0.5 kg/mol (A4)-   Bluesil® FLD 47V50 (non-functional silicone oil) Viscosity 50 mPa.s,    MW approx 3 - 4 kg/mol (E1)-   Base Color 552 (supplied by Sioen) = white base color based on TiO₂    (F1)-   Silane 51005 - advanced or partially condensed ethyl silicate    (SiOEt₄), tetraethyl ester, hydrolyzed (AR1)-   Dynasilan® P (supplied by Evonik) or propyl silicate or tetra    n-propylorthosilicate or tetrapropyl orthosilicate (AR2)-   Mediaplast® VP 5071/A (supplied by Kettlitz Chemie)mixture of    polyalkylbenzene and high molecular weight hydrocarbons (comprises    between 25% and 50% of alkylbenzene (C10-C13)) (H1)-   Dimethyltin neodecanoate (supplied by Momentive) Decylamine CAS    2016-57-1 (supplied by Sigma-Aldrich) (C1)-   Dodecylamine CAS 124-22-1 (supplied by Sigma-Aldrich) (C2)-   Dibutylamine CAS 111-92-2 (supplied by Sigma-Aldrich) (C3)-   Dihexylamine CAS 143-16-8 (supplied by Sigma-Aldrich) (C4)-   Dioctylamine CAS 1120-48-5 (supplied by Sigma-Aldrich) (C5)-   Diisononylamine CAS 28454-70-8 (supplied by Sigma-Aldrich) (C6)-   Didodecylamine CAS 3007-31-6 (supplied by Sigma-Aldrich) (C7)-   Didecylamine CAS 1120-49-6 (supplied by Sigma-Aldrich) (C8)

2) Preparation of Examples in Accordance With the Invention andComparative Examples

In all of the compositions, the percentages (%) mentioned are expressedby weight with respect to the total weight of all of the constituents ofthe formulation.

The bicomponent precursors of the polyorganosiloxane compositions thatcan be vulcanized to silicone elastomers were composed of a part P1 anda part P2.

Preparation of Parts P1

The various constituents of part P1 were mixed using a DAC400speed-mixer type appliance or using a propeller in a plastic pot.

TABLE 1 Composition of parts P1 Composition Part P1--1 Part P1 -- 2Paste 60.2 60.2 Sifraco E600 18 18 48V3500 20 - 48V14000 - 20 Base Color552 0.5 0.5 48V750 1 1 Bluesil RP 120PA 0.2 0.2 Water 0.1 0.1 Total 100100

Preparation of Parts P2

The various constituents of parts P2 were manually mixed in a glassflask.

TABLE 2 Part P2 for comparative examples Part P2 Reference Part P2-C1for comparative test C1 Part P2-C2 for comparative test C2 Part P2-C3for comparative test C3 Catalyst 6.6 2.11 2.49 Dimethyltin naodecanoateDecylamine Dodecylamine Silane 51005 40 35 35 Propyl silicate 5.3 5.3Mediaplast VP 5071/A 12.95 13.96 13.87 47V50 40.45 43.63 43.34 Total 100100 100

TABLE 3 Part P2 for examples in accordance with the invention ReferenceP2-1 P2-2 P2-3 P2-4 P2-5 P2-6 P2-7 P2-8 P2-9 P2-10 Catalyst 3.62 3.623.24 3.47 2.49 4 9.5 1.74 2.49 4 Diisononyl amine Diisononyl amineDioctyl amine Dibutyl amine Dihexyl amine Didecyl amine Didodecyl amineDibutyl amine Dihexyl amine Didecyl amine Silane 51005 40 35 35 40 35 4040 35 40 35 Propyl silicate 5.3 5.3 5.3 5.3 5.3 Mediaplast VP 5071/A13.67 13.6 13.69 13.7 13.87 13.58 12.24 14.06 13.94 13.5 47V50 42.7142.48 42.77 42.83 43.34 42.42 38.26 43.9 43.57 42.2 Total 100 100 100100 100 100 100 100 100 100

Preparation of Mixtures P1 + P2

The parts P1 and P2 employed in the comparative bicomponent systemsdenoted Ck, in which k is 1 to 3, and the bicomponent systems inaccordance with the invention, denoted Ex.m, in which m is from 1 to 11,are detailed in Table 4.

TABLE 4 Composition of bicomponent systems Bicomponent reference P1+P2C1 C2 C3 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Ex. 9 Ex. 10Ex. 11 Part P1 P1 - 1 P1 - 1 P1 -1 P1 -1 P1 -1 P1 - 1 P1 -1 P1 - 1 P1 -1P1 - 1 P1 -1 P1 -2 P1 -1 P1 - 2 Part P2 P2 -C1 P2 -C2 P2 -C3 P2 - 1 P2-2 P2 -3 P2 -4 P2 -5 P2 -6 P2 -7 P2 -8 P2 -9 P2 -10 P2 -11

Part P1 and part P2 were mixed with a spatula for three minutes, thenwith a speed mixer (planetary mixer) for twenty seconds at 1800 rpm. Themixture was then vacuum degassed so that there were no defects(bubbles).

The weight ratio was 100 parts of P1 to 5 parts of P2.

Preparation of Negative Molds Produced From Silicone Elastomer

Negative molds were produced by applying the pre-mixed formulation(mixture of part P1 and of part P2) to a master to be duplicated placedat the bottom of a pot.

45 g of part P1 and 2.25 g of part P2 were mixed with a spatula forthree minutes then with a speed mixer for twenty seconds at 1800 rpm.The mixture was then degassed under a vacuum bell jar for 5 minutes sothat there were no defects (bubbles, air incorporated during mixing withthe spatula) in the negative mold.

A master (parallelepipedal rectangle with a height of 8 mm; a width of35 mm, and a length of 35 mm) to be duplicated was placed and centeredat the bottom of a plastic pot (which had been degreased with ethanol)with a height of 27 mm and an internal diameter of 63 mm.

The master + pot were tared and between 40 and 42 g of the formulationP1 + P2 was applied to the master.

The control negative molds denoted MN Ck, in which k was from 1 to 3,and the negative molds in accordance with the invention, denoted MN m,in which m was from 1 to 11, were obtained after curing the mixturesP1 + P2. The mixture was allowed to cure at 23° C. for 24 hours. Thenegative mold produced from silicone elastomer was separated from themaster to be duplicated.

TABLE 5 Reference for control negative molds and negative molds inaccordance with the invention Reference negative mold MR C1 MN C2 MN C3MN 1 MN 2 MN 3 MN 4 MN 5 MN 6 MN 7 MN 8 MN 9 MN 10 MN 11 Referencemixture P1+P2 C1 C2 C3 Ex. 1 Ex. 2 Ex. 3 EX. 4 Ex. 5 EX. 6 EX. Ex. 8 Ex.9 Ex. 10 Ex. 11

Preparation of Replicas

The negative molds produced from silicone elastomer were filled a firsttime with polyurethane casting resin (reproduction material).

F190 Fastcast polyurethane resin from Axson was prepared in transparentplastic pots (so that the homogeneity of the mixture could be observed)with a height of 48 mm and an internal diameter of 51 mm. The polyolpart was charged and underwent decantation; it was therefore mixed witha spatula prior to use (homogeneous color and appearance withoutsedimentation at the bottom of the receptacle). This operation was easyto carry out manually.

12.5 g ± 0.1 g of the polyol part (white color) and 12.5 g ± 0.1 g ofthe isocyanate part (brown color) were weighed out. The two parts weremixed with a spatula for one minute, checking the homogeneity of themixture (a yellow colored mixture was obtained). Two negative molds werethen filled with this preparation (the cavity corresponding to themaster to be duplicated was filled to the rim).

The reproduction material was allowed to harden for 90 minutes atambient temperature inside the silicone negative molds in order toproduce a first replica.

The replica was separated from the silicone negative mold by detachingeach rim of the negative mold. If no adhesion to the negative mold wasobserved, a new replica was prepared and so on until the negative moldproduced from silicone elastomer deteriorated.

3) Characterization Characterization Tests for Mixture P1+P2

The properties of the mixture P1+P2 allowing molds to be produced fromsilicone elastomers were characterized by a pot life and curing kineticsexpressed in Shore A Hardness.

In addition, the silicone elastomer must not adhere to the master inorder to facilitate its removal from the mold. A large number ofdemolding operations is an indication of great durability of thesilicone elastomer mold.

Measurement of Pot Life (with a “Techne Gelation Timer GT3”) inAccordance With the French Standard NF T 77 107

A 22 mm, diameter plunger weighing 11.4 g immersed in a sample isactuated with an alternating vertical movement with a period of oneminute. When the consistency of the product is sufficient to support theweight of the disk for ½ minute, the gel point has been reached. Anelectrical contact then stops the timer started at the beginning of thetest. This time, expressed in minutes (min), is then taken to be the potlife. A pot life of between 20 and 200 min is desired.

Measurement of Curing Kinetics

The curing kinetics were evaluated using the Shore A hardness (SAH) inaccordance with the standards DIN 53505 and ISO 868. This hardness isgenerally measured 24 hours then 4 days and then 14 days after mixingthe parts P1 + P2. A hardness after 24 h equal to at least 68% of thefinal hardness at 14 days was desired. Hardnesses above and below theindenter are measured in order to evaluate the homogeneity of curing.Preferably, a difference of 2 Shore A or less is desired.

Post-curing expresses the difference in hardness between 14 days and 4days: a difference of 2 Shore A or less is desired for below theindenter.

Tests for Adhesion of Silicone Elastomer Mold to Master to be Reproduced

Masters to be duplicated formed from different materials were used inorder to evaluate the development of adhesion of the silicone elastomerduring the preparation of the negative mold.

The evaluated materials were: an organic plastic, namely polyurethane,and plaster. For each of the materials, the master used was aparallelepipedal rectangle with a height of 8 mm, a width of 35 mm and alength of 35 mm. The surface of this part was smooth.

After 24 hours, adhesion of the negative mold to the master wasevaluated qualitatively during demolding. Demolding of the master wascarried out by detaching each rim of the negative mold, one after theother, in order to evaluate the resistance to demolding.

If there was no resistance, the adhesion was evaluated at 0.

If a slight force had to be applied in order to remove the master, theadhesion was evaluated as +.

If a large force had to be applied in order to remove the master, but itwas possible to remove the master without tearing the silicone mold, theadhesion was evaluated as ++.

When it was not possible to demold the master without tearing thesilicone mold, the adhesion was evaluated as +++.

A mark of 0 or + was desired in order to use the negative mold for thepreparation of replicas.

Demolding Test

The master used was a parallelepipedal rectangle produced from metalwith a height of 8 mm, a width of 35 mm and a length of 35 mm. Thesurface of this part was smooth.

The test molds were produced in a method for casting the pre-mixedformulation (mixture of part P1 and of part P2) onto the metal partplaced at the bottom of a pot.

After 24 hours, the master was demolded.

Six days after demolding the master, the negative molds were filled forthe first time with polyurethane casting resin (reproduction material).

The polyurethane resin used to evaluate the resistance of the siliconeelastomer negative mold was Fastcast F190 resin from Axson. This resinis in the form of a bicomponent product which, once mixed at ambienttemperature (1:1 mixture), has a pot life of 8 minutes and can bedemolded after 90 minutes.

Next, between 3 and 5 polyurethane replicas were produced each day, eachtime with approximately 12.5 g of polyurethane resin. Each time, thereplicas molded from resin were left in the silicone elastomer negativemold for a minimum of 1.5 hours in order to obtain completepolymerization.

Demolding of the molded resin replicas was carried out by detaching eachrim of the silicone elastomer negative mold, one after the other, inorder to evaluate the resistance to demolding.

The number of reproductions which were obtained without degradation ofthe silicone elastomer negative mold (i.e. without tearing off smallpieces of silicone) is presented in one of the tables below. Thisenables the polyurethane resistance of the various silicone elastomernegative molds to be compared.

The results of the various tests carried out were as follows:

TABLE 6 The appearance of part P2 was observed visually. ReferenceNature of catalyst Observations, part P2 P2-C1 Dimethyltin neodecanoateTransparent single phase liquid P2-C2 Decylamine Transparent singlephase liquid P2-C3 Dodecylamine Liquid/solid, two-phase P2-1Diisononylamine Transparent single-phase liquid P2-2 DiisononylamineTransparent single-phase liquid P2-3 Dioctylamine Transparentsingle-phase liquid P2-4 Dibutylamine Transparent single-phase liquidP2-5 Dihexyl amine Transparet single-phase liquid P2-6 DidecylamineTransparent single-phase liquid P2-7 Didodecylamine Liquid/solid,two-phase

TABLE 7 Curing kinetics Reference Nature of catalyst Pot life (min) SAHPost-curing SAH 24h x 100/SAH 14d (%) 24h 4 days 14 days Below AboveBelow Above Below Above C1 Dimethyltin neodecanoate 193 19 23 27 28 2828 +1 68 C2 Decylamine 669 Not cured NM Too soft. NM Too soft. NM 16 16At 24 hrs, not yet cured C3 Dodecylamine 669 Not cured NM Too soft . NM14 14 At 24 hrs, not yet cured EX. 1 Diisononylamine 90 19 20 24 25 2626 +2 73 Ex. 2 Diisononylamine 120 18 18 23 24 24 25 +1 75 Ex. 3Dioctylamine 125 18 17 23 24 25 26 +2 72 Ex. 4 Dibutylamine 68 18 16 2322 25 23 +2 72 EX. 5 Dihexylamine 134 17 17 23 23 24 25 +1 71 Ex. 6Didecylamine 109 17 18 23 24 25 26 +2 68 Ex. 7 Didodecylamine 92 19 2024 25 25 26 +1 76 Ex. 10 Didecylamine 124 17 17 23 24 25 26 +2 68

TABLE 8 Results of test for evaluating the adhesion of the siliconeelastomer negative mold to different masters Reference for negative moldComposition employed during manufacture of negative mold Nature ofcatalyst used in the composition Adhesion of silicone negative mold topolyurethane (PU) master to plaster master MN C1 C1 Dimethyltinneodecanoate 0 0 MN C2 C2 Decylamine +++ MN C3 C3 Dodecylamine +++ +++MN 2 Ex. 2 Diisononylamine 0 0 MN 3 Ex. 3 Dioctylamine + 0 MN 5 Ex. 5Dihexylamine 0 MN 8 Ex. 8 Dibutylamine ++ +++ MN10 Ex. 10 Didecylamine 00

TABLE 9 Number of successive molding/demolding cycles (durability ofsilicone elastomer mold) Reference for negative mold Compositionemployed during manufacture of negative mold Nature of catalyst used inthe composition Number of successive moldings/demoldings of articlesmolded from PU MN C1 C1 Dimethyltin neodecanoate 37 MN C2 C2 DecylamineSticks to master - not evaluated MN C3 C3 Dodecylamine Sticks tomaster - not evaluated MN 1 Ex. 1 Diisononylamine 46 MN 2 Ex. 2Diisononylamine 41 MN 3 Ex. 3 Dioctylamine 47 MN 8 Ex. 8 Dibutylamine 58MN 9 Ex. 9 Dihexylamine 52 MN 11 Ex. 11 Diisononylamine 54

In conclusion, the catalysts employed in the silicone compositions usedduring the preparation of silicone elastomer molds in accordance withthe invention can be used to simultaneously obtain:

-   a sufficiently long pot life to use the part P1 + part P2 mixture    (between 20 and 200 min),-   “fast” curing (post-curing a maximum +2 and SAH ratio of 24h x    100/SAH 14 days > 68%),-   -silicone elastomer molds obtained using the method in accordance    with the invention which can be used to mold a large number of    parts, for example from polyurethane (number of successive    molding/demolding cycles > 37), and all this in the absence of    tin-based compounds.

In order to satisfy the supplemental conditions that the part containingthe catalyst must be homogeneous (transparent single phase) and that thesilicone elastomer negative molds obtained by the method in accordancewith the invention must not adhere to the master even in the absence ofrelease agent applied to the master to be reproduced, thepolycondensation catalysts C satisfy the general formula (I):

in which the symbols R″, which may be identical or different, representaliphatic hydrocarbon radicals containing 6 to 10 carbon atoms.

1. (canceled)
 2. (canceled)
 3. (canceled)
 4. A polyorganosiloxanecomposition X that can be cured into an elastomer by polycondensationreactions, wherein the composition X does not contain a metalliccatalyst and comprises: a silicone base B comprising at least onepolyorganosiloxane oil A that can be cured by a polycondensationreaction in a manner such as to form a silicone elastomer, and acatalytic quantity of at least one polycondensation catalyst C which isan organic compound having a general formula (I):

in which the symbols R″, which are identical or different, representaliphatic hydrocarbon radicals containing 6 to 10 carbon atoms.
 5. Anegative mold MN produced from silicone elastomer by: a) preparing apolyorganosiloxane composition X that can be cured to produce anelastomer by polycondensation reactions, which does not contain ametallic catalyst, and comprising: a silicone base B comprising at leastone polyorganosiloxane oil A that can be cured by a polycondensationreaction, and a catalytic quantity of at least one polycondensationcatalyst C, which is an organic compound having a general formula (I):

in which the symbols R″, which are identical or different, representaliphatic hydrocarbon radicals containing 1 to 30 carbon atoms, b)applying said polyorganosiloxane X to a master to be duplicated,optionally already covered with a release agent, c) curing saidpolyorganosiloxane composition X in the presence of moisture supplied byambient air or by a prior addition of water, in order to form thenegative mold MN produced from silicone elastomer, which is animpression corresponding to the exterior contour of the master to beduplicated, and d) separating the negative mold MN produced fromsilicone elastomer from the master to be duplicated.
 6. (canceled)
 7. Amethod of manufacturing a molded article, the method comprising: a)preparing a negative mold comprising: i) preparing a polyorganosiloxanecomposition X that can be cured to produce an elastomer bypolycondensation reactions, which does not contain a metallic catalyst,and comprising: a silicone base B comprising at least onepolyorganosiloxane oil A that can be cured by a polycondensationreaction, and a catalytically effective quantity of at least onepolycondensation catalyst C, which is an organic compound having thegeneral formula (I):

in which the symbols R″, which are identical or different, representaliphatic hydrocarbon radicals containing 1 to 30 carbon atoms, ii)applying said polyorganosiloxane X to a master to be duplicated,optionally already covered with a release agent, iii) curing saidpolyorganosiloxane composition X in the presence of moisture supplied byambient air or by a prior addition of water, in order to form thenegative mold MN produced from silicone elastomer, which is animpression corresponding to the exterior contour of the master to beduplicated, and iv) separating the negative mold MN produced fromsilicone elastomer from the master to be duplicated and b) applying areproduction material to the negative mold MN.
 8. The method of claim 7,further comprising: c) allowing the reproduction material to hardeninside the negative mold MN produced from silicone elastomer, in orderto produce a replica R of the master to be duplicated, and d) separatingthe replica R from the negative mold MN produced from siliconeelastomer, wherein steps c) and d) are performed sequentially after stepb.
 9. The negative mold MN of claim 5, wherein in step c), thehomogeneity of curing, as determined by measuring the Shore A hardnessabove and below the indenter and the difference is 2 or less.
 10. Themethod of claim 7, wherein the at least one polyorganosiloxane oil Acomprises a reactive α,ω-dihydroxydiorganopolysiloxane polymer havingthe general formula:

in which the substituents R ¹, which may be identical or different, eachrepresent a monovalent C₁ to C₁₃ hydrocarbon, which may or may not besaturated, which may or may not be substituted, aliphatic, cyclic oraromatic, and n has a sufficient value to provide theα,ω-dihydroxydiorganopolysiloxane polymer with a dynamic viscosity at25° C. of 10 to 1000000 mPas.
 11. The method of claim 10, wherein the atleast one polyorganosiloxane oil A has a dynamic viscosity at 25° C. offrom 50 to 200000 mPas.
 12. The method of claim 10, wherein at least 60%by number of the radicals R¹ are methyl radicals.
 13. The method ofclaim 10, where the radicals R¹ that are not methyl radicals are phenyland/or vinyl radicals.
 14. The method of claim 7, wherein thepolyorganosiloxane composition X comprises: (a) a silicone base that iscapable of hardening into a silicone elastomer in the presence of acatalyst by polycondensation reactions, comprising: for 100 parts byweight of at least one α, ω-dihydroxydiorganopolysiloxane A, 0.1 to 60parts by weight of at least one curing agent AR, and 0.001 to 10 partsby weight of water, and (b) a catalytically effective quantity of apolycondensation catalyst C.
 15. The method of claim 14, wherein thecuring agent AR is: a) a silane with the general formula (2):

in which the symbols R³, which may be identical or different, representalkyl radicals containing 1 to 8 carbon atoms, or C₃-C₆ oxyalkyleneradicals, the symbols R² representing a saturated or unsaturated, linearor branched aliphatic hydrocarbon group, a saturated or unsaturatedand/or aromatic, monocyclic or polycyclic carbocyclic group, and k isequal to 0 or 1; and b) partial hydrolysis and condensation products ofa silane with formula (2).
 16. The method of claim 14, wherein 0.1 to 6parts by weight of curing agent AR are used per 100 parts by weight ofthe at least one polyorganosiloxane oil A.
 17. The method of claim 12,wherein the compositions further comprises reinforcing fillers,semi-reinforcing fillers or packing fillers CH.
 18. The method of claim17, wherein the reinforcing fillers are fumed silicas or precipitatedsilicones having a specific surface area, measured using a BET method,of at least 50 m²/g, a mean primary particle dimension of less than 0.1µm (micrometers) and an apparent density of less than 200 g/liter. 19.The method of claim 17, wherein the semi-reinforcing fillers or packingfillers are selected from ground quartz, calcined clays and diatomaceousearth and have a particle diameter of more than 0.1 µm.